The Chemistry, Recrystallization and Thermal Expansion of Brannerite from Akchatau, Kazakhstan

Numerous studies expose the potential of brannerite to become a good matrix, concentrating fission products and actinides. Minerals can complement the data collected from the synthetic materials and offer an advantage of a long-time exposure to radiation. Natural metamict brannerite from Akchatau, Kazakhstan, and its annealed sample were studied by EPMA, Raman spectroscopy, TGA, DSC, XRD and HTXRD. The radioactivity of pristine and annealed samples of brannerite was measured. Brannerite from Akchatau is characterized by the absence of significant amounts of REE and yttrium. The studied brannerite regains its structure at a temperature ~650 °C, revealed by the HTXRD and DSC. HTXRD was also performed on the annealed recrystallized brannerite. The thermal expansion for brannerite has been determined for the first time. The brannerite structure expands anisotropically with temperature increase. All the thermal expansion coefficients are positive except for αβ. The decreasing beta parameter indicates a “shear structural deformation“. The angle between the 1st axis of the tensor and the crystallographic a axis decreases with the increase of the temperature. The structure expands mostly in the α11 direction, approaching the bisector of the β angle. Brannerite has a low CTE at room temperature—αv = 16 × 10−6 °C−1, which increases up to 39.4 × 10−6 °C−1 at 1100 °C. In general, the thermal stability of brannerite is comparable to that of the other perspective oxide radioactive waste-immobilizing matrices (e.g., Ln2Zr2O7, CePO4, CaTiO3, CaZrTi2O7). The calculated thermal expansion of brannerite and the understanding of its underlying crystal chemical mechanisms may contribute to the behavior prediction of the material (both metamict and crystalline) at high temperatures.


Introduction
Brannerite is a uranium titanate mineral with an ideal formula of UTi 2 O 6 . It ideally contains 62.8 wt.% UO 2 [1,2]. The high content of uranium makes brannerite an exploitable uranium resource. It contains uranium in a multivalent state due to its origin [3] and redox reactions are caused by the radioactive decay. Therefore, tetra-, penta-and hexavalent uranium are able to incorporate into the natural and synthetic brannerite [4,5]. ThO 2 is a common component of the natural brannerite, along with up to 8 wt.% of rare earth elements and a small amount of CaO, Fe 2 O 3 , PbO and Al 2 O 3 [3,6]. Due to the hydration and alteration, the significant amounts of Si and other elements are able to be incorporated into the structure [7]. Thus, the mineral has the general formula of AB 2 O 6 , where the A site can be occupied by U, Ca, Th, Y and REE, and the B site is mainly occupied by Ti, Nb, Si, Fe and Al [1,3,7]. The highly radioactive, uranium-bearing mineral was first found in a gold placer in Idaho, USA [8]. As an accessory mineral, brannerite is very stable and can be found in various geological environments, including granites, granitic pegmatites and hydrothermally altered sedimentary rocks. The deposit Crocker's Well in South Australia is related to the late tectonic granitoid intrusions, pegmatitic brannerite is usually found in association with Ti oxides, mainly rutile and U-Th-rich silicates [3]. Low-temperature Au deposits at Witwatersrand (South Africa) may also be a source of brannerite, where brannerite is considered as a secondary uranium mineral, it appears as an inclusion in detrital minerals, linings around pyrobitumen nodules and micro veins in gold-bearing horizons [9]. The occurrence of brannerite in the Central African Orogenic Belt is related to post-magmatic metamorphism, and the minerals associated with brannerite are monazite, uraninite, zircon, albite, calcite, chlorite, apatite, U-silicates and iron oxides [10]. The Hüttenberg deposit is an Eastern Alps Cretaceous siderite deposit where brannerite exhibits euhedral prismatic crystals and shows the evidence of hydration, metamictization and alteration to anatase [11]. Brannerite is reported also in altered ores at the uranium deposit Komsomolskoye, Central Kazakhstan [12]. In this work, reported below, the brannerite sample ( Figure 1b) originates from the Akchatau, Kazakhstan, where the W-Mo deposits are hosted within leucocratic granites of the Permian age [13].
Brannerite is a refractory titanate, and extraction of the uranium requires more intense leaching conditions than typical uranium oxide ores. However, on the other side, the stable titanate structure can be used in material science. Brannerite-based synthetics have been widely studied. Much research exposes brannerite's potential to become a matrix, concentrating fission products and actinides. It, therefore, can be used for radioactive Figure 1. General projection of the crystal structure of brannerite along the b axis (UO 6 = yellow octahedra; TiO 6 = blue octahedra; structure drawing is based on data reported in Szymanski and Scott [2]) (a). Brannerite (black massive grains) in a host rock from Akchatau (Kazakhstan) (b).
The highly radioactive, uranium-bearing mineral was first found in a gold placer in Idaho, USA [8]. As an accessory mineral, brannerite is very stable and can be found in various geological environments, including granites, granitic pegmatites and hydrothermally altered sedimentary rocks. The deposit Crocker's Well in South Australia is related to the late tectonic granitoid intrusions, pegmatitic brannerite is usually found in association with Ti oxides, mainly rutile and U-Th-rich silicates [3]. Low-temperature Au deposits at Witwatersrand (South Africa) may also be a source of brannerite, where brannerite is considered as a secondary uranium mineral, it appears as an inclusion in detrital minerals, linings around pyrobitumen nodules and micro veins in gold-bearing horizons [9]. The occurrence of brannerite in the Central African Orogenic Belt is related to post-magmatic metamorphism, and the minerals associated with brannerite are monazite, uraninite, zircon, albite, calcite, chlorite, apatite, U-silicates and iron oxides [10]. The Hüttenberg deposit is an Eastern Alps Cretaceous siderite deposit where brannerite exhibits euhedral prismatic crystals and shows the evidence of hydration, metamictization and alteration to anatase [11]. Brannerite is reported also in altered ores at the uranium deposit Komsomolskoye, Central Kazakhstan [12]. In this work, reported below, the brannerite sample ( Figure 1b) originates from the Akchatau, Kazakhstan, where the W-Mo deposits are hosted within leucocratic granites of the Permian age [13].
Brannerite is a refractory titanate, and extraction of the uranium requires more intense leaching conditions than typical uranium oxide ores. However, on the other side, the stable titanate structure can be used in material science. Brannerite-based synthetics have been widely studied. Much research exposes brannerite's potential to become a matrix, concentrating fission products and actinides. It, therefore, can be used for radioactive waste immobilization. Exploration of brannerite synthesis techniques can provide new insights for the immobilization of radionuclides [14]. The solid phase method, commonly used for ceramic syntheses, is based on the firing of a mixture of uranium and titanium dioxides at temperatures in the range 1300-1400 • C [15]. The crystals used by Szymanski and Scott [2] for the structure determination were grown by a cryolite fusion technique. The wet chemistry route is also adopted for brannerite synthesis [14,16]. To avoid the leakage of hazardous elements from the complex ceramics to the environments, it is important to determine the thermal expansion characteristics of the matrix. Minerals can complement the data collected from the synthetic materials and offer an advantage of a long-term exposure to the radiation. The aim of this work was to study a natural brannerite; however, since the mineral samples are metamict, their recrystallization was studied. The thermal expansion of the crystalline brannerite is reported for the first time.

Sample
Samples of brannerite were obtained from the Mineralogical Museum of Saint Petersburg University, Russia. The mineral sample is from the Akchatau (Kazakhstan) greisen W-Mo deposit. Brannerite is represented by metamict grains up to 2 mm in length ( Figure 1b). Brannerite grains were handpicked and investigated under the optical microscope to avoid the presence of the impurities of other minerals.
The heating of metamict brannerite grains for the subsequent studies was carried out in platinum crucibles at a temperature of 1200 • C in a laboratory furnace produced by Nabertherm.

Quantitative EMPA
The metamict and heated brannerite grains were prepared by mounting them in an epoxy resin. The samples were studied using the scanning electron microscope Hitachi S-3400N, equipped with a spectrometer, Oxford Instruments X-Max 20, for energydispersion analysis. Photos of the samples were taken in the backscattered electron mode (BSE). Quantitative analyses were performed with an accelerating voltage of 20 kV and a beam current of 1.8 nA. Acquisition time is 30 s, with a resolution up to 4 nm. The following standards were used for the quantification: MAC (Micro Analysis Consultants Ltd., United Kingdom); Geller reference standards (Geller microanalytical laboratory)

Raman Spectroscopy
The metamict and annealed grains of brannerite were placed on the stage of an Olympus BX41 microscope, equipped with a Horiba Jobin-Yvon LabRam HR800 Raman spectrometer. Raman spectra were excited by an Ar + laser (457~514 nm) in the range 100-4000 cm −1 . Baseline correction was used to improve the signal-to-noise ratio.

X-ray Powder Diffraction
The heated and metamict samples were ground for the powder X-ray diffraction studies. Preliminary X-ray diffraction (XRD) analysis indicated that the investigated samples are metamict. The sample calcined in air at a temperature of 1200 • C for 6 h produced wellcrystallized phases. Preliminary XRD measurements at room temperature were carried out using a Rigaku Miniflex II diffractometer (Co-Kα, 30 kV, 15 mA).
The high-temperature X-ray (HT-XRD) experiments were performed using a Rigaku Ultima IV diffractometer with a thermal attachment (Co-Kα, 40 kV and 30 mA, reflection geometry, D/teX ultra-high-speed detector, air atmosphere, 2θ = 10-80 • , temperature range 25-1200 • C, step size 100 • C for the temperature range 20-600 • C and 25 • C for 600-1200 • C). HT-XRD measurements performed for metamict samples demonstrate the evolution of the structure during recrystallization, whereas the results obtained from the annealed sample provided the data for the thermal expansion calculation.

Thermal Investigations
Thermal analysis of the metamict brannerite was performed in air with a 20 • C/min heating rate, the powder sample was heated up to 1300 • C and subsequently cooled to 300 • C at the same rate. TGA and DSC curves were recorded using TA Instruments STA 429 CD.

Radioactivity Measurements
Measurements of the radioactivity exhibited by the studied brannerite were carried out. Gamma-ray spectra for 3.6 g of a sample were obtained and processed using the gammaspectrometer MKGB-1. The activity and specific activity of gamma-emitting radionuclides 232 Th, 226 Ra, 137 Cs и 40 K in the sample were determined. The radioactivity of the powder sample was repeatedly examined after its calcination in air at a temperature of 1200 • C for 6 h.

Chemical Composition and Phase Purity
Two pristine grains (Brn1 and Brn2) and one calcined grain (Brn3) were investigated by EPMA, the BSE image is shown in Figure 2.
geometry, D/teX ultra-high-speed detector, air atmosphere, 2θ = 10-80°, temperature range 25-1200 °C , step size 100 °C for the temperature range 20-600 °C and 25 °C for 600-1200 °C ). HT-XRD measurements performed for metamict samples demonstrate the evolution of the structure during recrystallization, whereas the results obtained from the annealed sample provided the data for the thermal expansion calculation.

Thermal Investigations
Thermal analysis of the metamict brannerite was performed in air with a 20 °C /min heating rate, the powder sample was heated up to 1300 °C and subsequently cooled to 300 °C at the same rate. TGA and DSC curves were recorded using TA Instruments STA 429 CD.

Radioactivity Measurements
Measurements of the radioactivity exhibited by the studied brannerite were carried out. Gamma-ray spectra for 3.6 g of a sample were obtained and processed using the gamma-spectrometer MKGB-1. The activity and specific activity of gamma-emitting radionuclides 232 Th, 226 Ra, 137 Cs и 40 K in the sample were determined. The radioactivity of the powder sample was repeatedly examined after its calcination in air at a temperature of 1200 °C for 6 h.

Brn1-Unheated
Brn2-Unheated Brn3-Heated According to the analysis, the Akchatau brannerite is close to the stoichiometric brannerite and contains a significant amount of thorium to form a solid solution with thorutite, ThTi 2 O 6 . Surprisingly, rare earth elements are not detected in studied samples. Total measured contents are close to 100%, water was not detected. The presence of small amounts of lead may originate as a decay product of the uranium series.

Oxides
Brn1 is a heterogenous brannerite, Figure 2 shows the contrast in the BSE intensity, indicating that the elements are unevenly distributed. Some areas show evidence of the alteration. The elongated section, spreading along the fracture, appears as "darker" BSE intensity in comparison with the overall grain. The analytic total of this area is reduced tõ 95%. The low amount shows that some lightweight, undetectable components concentrate here; meanwhile, the weight percentage of SiO 2 increases up to 0.5%. Other areas in Brn1 do not contain SiO 2 . Several rhombic crystals (5-8 µm) were identified as uranium-rich pyrochlore with~10% H 2 O (Figure 2a).
In addition to inclusions, little "bright white" spots of 0.4-3 µm in size can be seen in both grains (Figure 2, Brn1 and Brn2). Their composition cannot be determined unambiguously due to the capture of other elements from the surrounding brannerite matrix. Table 2 shows their average chemical composition with totals normalized to 100. High contents of PbO and S suggest it to be galena, PbS. The grain Brn2 is even less homogeneous compared to Brn1, Table 1 demonstrates its chemical composition based on 15 spot analyses. The grain Brn2 is characterized by the linearly altered zones, where the content of SiO 2 reaches 1.5-1.7 wt.% (Figure 2, Brn2).
The It can be seen that the chemical composition of brannerite fulfills the stoichiometry AB 2 O 6 , where A = U and Th; B = Ti and Fe. The localization of Si is not clear yet. It is presumed to occupy part of the B site as its atomic radius is closer to that of Ti rather than U.
Another grain, Brn3, was calcined in the atmosphere at 1200 • C for 4 h. Its chemical composition is also listed in Table 2. The chemical composition of the annealed brannerite is similar to that of the metamict grain. Calcined brannerite apparently becomes homogeneous, although the texture shows increased porosity typical for recrystallized metamict minerals. Numerous bright spots (0.2-1 µm) are observed in the enlarged BSE image. However, their chemical content has not been successfully determined due to their small size.

Raman Spectroscopy
Raman spectroscopy was used to investigate both the metamict and annealed brannerite. Frost and Beddy [17] compared the Raman spectra of brannerite and uranyl oxyhydroxide hydrates; they attributed the observed bands to the (UO 2 ) 2+ and TiO stretching and bending vibrations, as well as U-OH and O-Ti-O bending vibrations. Charalambous and coauthors [7] examined partially metamict brannerite, the Raman spectra of metamict minerals exhibited broad bands in the range of 50-1100 cm −1 . Zhang and coauthors [18] obtained Raman spectra of natural and synthetic brannerite and recognized some incorrect Raman assignments performed in previous works.
We obtained Raman spectra in the 90-3500 cm −1 range for both metamict and annealed samples. The Raman spectrum of the metamict brannerite shows only a few broad and overlapping bands (Figure 3a). Raman bands are observed only in the range 90-1200 cm −1 .
The mineral structure is heavily damaged. However, the Raman spectra of most areas perform neither O-H stretching of water molecules and hydroxyl groups at approximately 3500 cm −1 nor the O-H-O bending bands at around 1600 cm −1 . O-H bands are observed only in the areas close to the cracks (Figure 2c), which indicates the partial hydration and alteration.
Annealed brannerite grains are more homogeneous. The vibrational modes are very intense and sharp in the Raman spectra (Figure 3b). The brannerite spectrum is in excellent agreement with the Raman spectrum of the annealed brannerite provided in the previous work of Zhang et al. [18]. The comparison of the obtained data with the reference data is provided in Table 3.

X-ray Powder Diffraction
To identify the recrystallization temperature and to observe, in situ, the crystallization of brannerite, X-ray powder diffraction was performed for the metamict sample. Figure 4 demonstrates the structural evolution of the metamict brannerite with increasing temperature. Pt holder diffraction peaks and unknown impurity were observed during the entire heating process.  Annealed brannerite grains are more homogeneous. The vibrational modes are very intense and sharp in the Raman spectra (Figure 3b). The brannerite spectrum is in excellent agreement with the Raman spectrum of the annealed brannerite provided in the previous work of Zhang et al. [18]. The comparison of the obtained data with the reference data is provided in Table 3.   Table 3. Raman bands and their assignment in the annealed studied brannerite sample and the reference data from [18,19]. Previous research shows that the temperature of the brannerite from Crocker Well (South Australia) recrystallization is in the range of 800-900 • C [7]. Adler and Puig [20] determined the start of brannerite recrystallization above 550 • C. The brannerite from El Cabril mine (Spain) completely recrystallizes between 900 • C and 1100 • C, but the crystallization process starts earlier, in the range 500-700 • C [21]. However, our in situ studies reveal that brannerite from Akchatau recrystallizes at a temperature as low as 625-650 • C.

This Study
At temperatures above 625 • C, several diffraction peaks quickly evolve, indicating the start of the recrystallization process. the entire heating process.
Previous research shows that the temperature of the brannerite from Crocker Well (South Australia) recrystallization is in the range of 800-900 °C [7]. Adler and Puig [20] determined the start of brannerite recrystallization above 550 °C . The brannerite from El Cabril mine (Spain) completely recrystallizes between 900 °C and 1100 °C , but the crystallization process starts earlier, in the range 500 °C -700 °C [21]. However, our in situ studies reveal that brannerite from Akchatau recrystallizes at a temperature as low as 625-650 °C . At temperatures above 625 °C , several diffraction peaks quickly evolve, indicating the start of the recrystallization process. There are some previously published data showing that TiO2 and U3O8 can be produced during the recrystallization of the brannerite-type material, when the stoichiometric material is heated in the air [15]. Uranium oxides appear at ~ 800 °C : diffraction lines 25°, 31.5° and 40° 2θ can be assigned to U3O8 (ICSD-51525). This phase, however, disappears at ~ 900 °C and evolves into the uraninite-type structure UO2 (ICSD-61576). It is known that U3O8 decomposes into UO2, with the temperature increase even under mildly reducing conditions [22,23]. Figure 5 shows the ratio of thus formed U3O8 and UO2 with the temperature increase. The diffraction pattern of the sample after cooling shows that the oxides may present only There are some previously published data showing that TiO 2 and U 3 O 8 can be produced during the recrystallization of the brannerite-type material, when the stoichiometric material is heated in the air [15]. Uranium oxides appear at~800 • C: diffraction lines 25 • , 31.5 • and 40 • 2θ can be assigned to U 3 O 8 (ICSD-51525). This phase, however, disappears at~900 • C and evolves into the uraninite-type structure UO 2 (ICSD-61576). It is known that U 3 O 8 decomposes into UO 2 , with the temperature increase even under mildly reducing conditions [22,23]. Figure 5 shows the ratio of thus formed U 3 O 8 and UO 2 with the temperature increase. The diffraction pattern of the sample after cooling shows that the oxides may present only at the levels below the detection limits. In addition, the rutile phase is also noted in the annealed sample. Rutile, TiO 2 , is typically associated with brannerite-rich ores in natural environments. The R-factors calculated by the Rietveld refinement increase with the temperature rise and fluctuate in the range of 6.2-12.6%.

Thermal Expansion
High-temperature powder diffraction experiments were performed on the annealed brannerite ( Figure 6). The program "Rietveld to tensor" [24] was used to analyze the XRD data and to calculate the thermal expansion.
Lattice parameters of brannerite were calculated using the Rietveld Method. The structure expands mostly along the a axis, while along the b axis the changes are very minor. Unit cell parameters a, b and c increase in the range 9.82-9.92 Å, 3.74-3.77 Å and 6.88 to 6.94 Å, respectively. The β angle decreases slightly between 118.6 and 118.1 • . The unit cell volume increases from 221.89 to 228.83 Å 3 (Figure 7). The temperature dependence of the unit cell parameters was approximated by polynomials of the second order: at the levels below the detection limits. In addition, the rutile phase is also noted in the annealed sample. Rutile, TiO2, is typically associated with brannerite-rich ores in natural environments. The R-factors calculated by the Rietveld refinement increase with the temperature rise and fluctuate in the range of 6.2-12.6%.

Thermal Expansion
High-temperature powder diffraction experiments were performed on the annealed brannerite ( Figure 6). The program "Rietveld to tensor" [24] was used to analyze the XRD data and to calculate the thermal expansion.  perature rise and fluctuate in the range of 6.2-12.6%.

Thermal Expansion
High-temperature powder diffraction experiments were performed on the annealed brannerite ( Figure 6). The program "Rietveld to tensor" [24] was used to analyze the XRD data and to calculate the thermal expansion.   Table 4 shows the obtained values. The value of the volumetric expansion α v is the sum of the eigenvalues α 11 , α 22 and α 33 . The linear expansion along the crystallographic axis b is α 22 . All the thermal expansion coefficients are positive except for α β . Decreasing parameter beta indicates a "shear structural deformation". This type of thermal deformation is typical for monoclinic crystals, as its thermal expansion is determined primarily by the change of the β angle. The angle between the 1st axis of the tensor and the crystallographic a axis decreases with the increase in the temperature; as a result, the structure expands mostly in the α 11 direction, approaching the bisector of the β angle (Figure 8b). Thermal expansion tensors of brannerite at different temperatures are shown in Figure 8a. The decreasing β angle value is demonstrated by the rotation of the crystallographic a axis towards the c axis.  Note, that the expansion along the a axis is higher, compared to α c , at temperatures below 500 • C; afterwards, α c exceeds α a in the range 500-1100 • C. The maximum expansion occurs along or close to the direction of the longer (weaker) bonds. The U-O bond is more sensitive to the temperature increase. The expansion of the UO 6 octahedra is more pronounced at the first stages of the heating. Its expansion drives the enlargement of the interlayer distance as UO 6 octahedra link two TiO 6 octahedral layers. Note, that the expansion along the a axis is higher, compared to αc, at temperatures below 500 °C ; afterwards, αc exceeds αa in the range 500 °C -1100 °C . The maximum expansion occurs along or close to the direction of the longer (weaker) bonds. The U-O bond is more sensitive to the temperature increase. The expansion of the UO6 octahedra is more pronounced at the first stages of the heating. Its expansion drives the enlargement of the interlayer distance as UO6 octahedra link two TiO6 octahedral layers.

Thermal Analysis
The results of the Differential Scanning Calorimetric (DSC) experiment and Thermal Gravimetric Analysis (TGA) of the metamict brannerite are shown in Figure 9. The DSC curve indicates two thermal transitions in the studied temperature range. With the temperature increases, metamict brannerite starts to recrystallize, which results in an exothermic peak at 670 °C . The endothermic peak at 1082 °C shows that the sample undergoes partial melting. The X-ray diffraction pattern of the studied sample after the thermal analysis and complete cooling indicates the formation of rutile.
The TG curve shows a mass decrease of 0.11% from 99 to 307 °C , corresponding to the loss of adsorbed water from the sample surface. The partial oxidation of Fe and U results in the TG curve upward trend from 444 to 1055 °C . The mass of the sample increases by 0.27% and 0.45% in the temperature ranges 444-643 °C and 670-834 °C ,

Thermal Analysis
The results of the Differential Scanning Calorimetric (DSC) experiment and Thermal Gravimetric Analysis (TGA) of the metamict brannerite are shown in Figure 9. The DSC curve indicates two thermal transitions in the studied temperature range. With the temperature increases, metamict brannerite starts to recrystallize, which results in an exothermic peak at 670 • C. The endothermic peak at 1082 • C shows that the sample undergoes partial melting. The X-ray diffraction pattern of the studied sample after the thermal analysis and complete cooling indicates the formation of rutile. To conclude, there is an increase in a sample mass due to the oxidation between 444 and 1055 °C . A strong exothermic process associated with the crystallization of brannerite is observed at 670 °C . The mass increase almost stops at the same time and continues only after the completion of the crystallization of brannerite. Brannerite starts to partially decompose after 1000 °C .

Measurements of the Radioactivity
The activity of the radionuclides 232 Th, 226 Ra, 137 Cs and 40 K was measured. The activity of the 137 Cs and 40 K isotopes was below the detection limit. The average value of 226 Ra activity was 10,900 Bq/g, which accounts for up to 96% of the total radioactivity; the total gamma activity of the sample was 11,350 Bq/g.
The radioactivity was measured again after the annealing in air at 1100 °C . The specific activity of 226 Ra decreased by 64% to 3396.07 Bq/g and the activity of 232 Th is 716.58 Bq/g. The total is 4957.59 Bq/g. The TG curve shows a mass decrease of 0.11% from 99 to 307 • C, corresponding to the loss of adsorbed water from the sample surface. The partial oxidation of Fe and U results in the TG curve upward trend from 444 to 1055 • C. The mass of the sample increases by 0.27% and 0.45% in the temperature ranges 444-643 • C and 670-834 • C, respectively.
A pause in the mass increase is observed in the range 643-670 • C, which implies several oxidation stages. The TG curve also demonstrates a slow mass increase by 0.17% in the range 834-1055 • C.
Between 1055 and 1115 • C, a mass loss of 0.60% is observed, which corresponds to the endothermic effect with a maximum at 1081 • C.
To conclude, there is an increase in a sample mass due to the oxidation between 444 and 1055 • C. A strong exothermic process associated with the crystallization of brannerite is observed at 670 • C. The mass increase almost stops at the same time and continues only after the completion of the crystallization of brannerite. Brannerite starts to partially decompose after 1000 • C.

Measurements of the Radioactivity
The activity of the radionuclides 232 Th, 226 Ra, 137 Cs and 40 K was measured. The activity of the 137 Cs and 40 K isotopes was below the detection limit. The average value of 226 Ra activity was 10,900 Bq/g, which accounts for up to 96% of the total radioactivity; the total gamma activity of the sample was 11,350 Bq/g.
The radioactivity was measured again after the annealing in air at 1100 • C. The specific activity of 226 Ra decreased by 64% to 3396.07 Bq/g and the activity of 232 Th is 716.58 Bq/g. The total is 4957.59 Bq/g.
Overall, these radioactive isotopes all belong to the uranium series. The heating procedure provokes the decrease of the radioactivity. It likely results from the escaping of some volatile isotopes from the sample, primarily radon. Radon may escape from the solid matrix at room temperature too; however, its emanation rates vary widely and are affected by the temperature, fission tracks and alpha-radiation damage. The small grain size of the powder sample promoted the radon diffusion.

Discussion and Concluding Remarks
Natural metamict brannerite from Akchatau, Kazakhstan, and its annealed sample were studied by EPMA and Raman spectroscopy to determine its chemical composition. The XRD and Raman spectra of the metamict brannerite indicated its structure to be heavily damaged. Iron and uranium are inhomogeneously distributed in the mineral due to the radiation damage. The studied metamict mineral grains show some zones enriched by the hydroxyl and SiO 2 . Pyrochlore and galena are found as inclusions. The crystal structure of brannerite is restored after annealing. The thermally processed brannerite's texture is porous and homogeneous.
The radioactivity of pristine and annealed samples of brannerite was measured. The specific activity of 226 Ra accounts for up to 96% of the total radioactivity, which indicates that the main type of a decay in the mineral sample belongs to the uranium series. The heating process results in the loss of nearly half of the radionuclides in brannerite.
XRD at high temperatures was performed for the metamict sample to investigate the recrystallization process in situ. It has been reported previously in several works that brannerite recrystallizes in the temperature range of 800-1000 • C [7,19,21,25]. In contrast, the studied brannerite from Akchatau regains its structure at a temperaturẽ 650 • C, approved also by the DSC measurements. We suggest that the recrystallization temperature is dependent mainly on the chemistry and homogeneity of the sample; but also depends on the degree of the radiation damage of the sample. Brannerite from Akchatau is characterized by the absence of the significant amounts of REE and yttrium typically observed at many other localities. The experimental conditions, such as a heating rate and annealing step, may also affect the recrystallization temperature. The HTXRD is recommended as a successful approach to identify, in detail, the recrystallization of the metamict minerals.
HTXRD was also performed on the annealed recrystallized brannerite. Thermal expansion of brannerite has been determined for the first time. The brannerite structure expands anisotropically with the temperature increase. The anisotropy is determined mainly by the change of the unit cell angles typical for monoclinic crystals. Despite its anisotropy, thermal expansion in brannerite is rather weak.
Considering that the waste immobilization form is usually a ceramic with various complex oxides, we can neglect the expansion anisotropy of single crystals when discussing the thermal expansion of the material. It is therefore reasonable to compare the volumetric CTE in brannerite with the available data for the other oxide materials. The Ln 2 Zr 2 O 7 and Ln 2 Hf 2 O 7 pyrochlores have volumetric expansion coefficients of 23.4-31.8 × 10 −6 • C −1 in the range 25-1400 • C [26]. The CePO 4 monazite expands very weakly, and its α v varies only slightly 21.0-27.4 × 10 −6 • C −1 in the range 25-700 • C [27]. Perovskite CaTiO 3 expands in a broader range: 37.87-55.37 × 10 −6 • C −1 in the temperature range 25-1000 • C [28]. The volumetric coefficients of the thermal expansion of zirconolite-3T CaZrTi 2 O 7 are 29.49-31.99 × 10 −6 • C −1 in the same temperature range [28]. Brannerite has a low CTE at room temperature-α v = 16 × 10 −6 • C −1 , which increases up to 39.4 × 10 −6 • C −1 at 1100 • C. In general, the thermal stability of brannerite is comparable to that of the other oxide radioactive waste-immobilizing matrices. Brannerite seems to be a promising material for such applications. Funding: R.C. was funded by the Region Hauts-de-France. Research was also supported within the scientific task # 0081-2022-0002.

Data Availability Statement:
The data can be provided by the authors upon request.